Precision corrosive salt spray chamber spot precision corrosive salt spray chamber spot corrosion test chamber Wuhan still testing Laboratory Equipment Co., corrosive salt spray chamber through the assessment of the material and its protective layer of salt spray corrosion, salt spray cycle , as well as similar protective layer of process quality comparison and assessment of the ability of some salt spray corrosion resistance; salt spray corrosion testing of the products made for parts, electronic components, metal material of the protective layer, as well as industrial products. Welded precision corrosive salt spray chamber box structure integrally molded at high temperature, corrosion-resistant, easy to clean, no leakage phenomenon. Tower spray system and filtration system equipped with a salt solution, no crystal nozzle, salt spray evenly distributed, the settlement amount of freedom to adjust. The lid transparent material clearly see box test items and spray. Using the structure of the water seal between the lid and the box, no salt overflow. Line control panel and other strength pieces were fixed in a position to facilitate inspection and maintenance the locks open style side door is not only beautiful, but also easy to maintain. Precision corrosive salt spray chamber Product Overview corrosive salt spray chamber the artificial salt spray environment conditions created by a major use of salt spray test equipment to assess the product or metal materials resistant to corrosion environmental testing. The salt spray test is a major use of salt spray test equipment created by the artificial salt spray environment conditions to assess the product or metal materials resistant to corrosion environmental testing. It is divided into two categories, a class of natural environmental exposure test, and the other is artificial the accelerated simulation salt spray environment test. The artificial salt spray environmental testing is the use of a certain volume of space test equipment - salt spray chamber, the volume of space within artificial assessment spray corrosion resistance quality of the product, resulting in a salt spray environment . Compared with the natural environment, the salt concentration of the chloride salt spray environment, can the general natural environment salt spray content several times or several times so that the corrosion speed is greatly increased, the product of the salt spray test, precision salt spray the results of corrosion test chamber at the time is also greatly reduced. If the natural exposed under the environment of a product sample to be tested, may have to wait until corrosion 1 year, and the in artificial salt spray under ambient conditions to test, as long as 24 hours, to give similar results. Neutral salt spray test is the emergence of the earliest applications of the most widely used accelerated corrosion test methods. It uses a 5% aqueous solution of sodium chloride salt, the solution of the PH value is adjusted in the neutral range (6 to 7) as a spray with the solution. Were taken to 35 ° C test temperature, to requirements the salt spray sedimentation rate between 1 ~ 2ml/80cm2.h. (2) copper accelerated acetic acid salt spray test is a newly developed abroad the rapid salt spray corrosion test, the test temperature of 50 ° C, add a small amount of copper salt - copper chloride salt solution, strongly evoked corrosion. Its corrosion rate is about 8 times the NSS test. (3) alternating salt spray test is a salt spray test, it is actually neutral salt spray test plus a constant humidity test. It is mainly used for the cavity-type machine products, penetration through the tide state environment, not only in the surface of the product of the salt spray corrosion, also inside the product. It is the product alternating two environmental conditions in the salt spray and the hot and humid conversion, whether the change in the electrical and mechanical properties of the final assessment of the whole products. (4) acetic acid salt spray test is of some glacial acetic acid, 5% sodium chloride solution was added to the PH value of the solution was reduced to about 3, and the solution becomes acidic, the final form of the salt from neutral salt spray into acidic. Its corrosion rate than the NSS test about three times faster. Wuhan is still testing inspection Equipment Co., Ltd. For more information please visit: company website: http://www.suncek.com Main products: corrosive salt spray chamber / high temperature chamber / low temperature test chamber / constant temperature test chamber / constant temperature and humidity Chambers / high and low temperature / alternating high and low temperature heat chamber / temperature shock test chamber / UV aging chamber / xenon arc lamp weather resistance test chamber / the ozone aging chamber / ventilation aging chamber / dust test chamber / rain test chamber / swing pipe rain test equipment / dripping test equipment / vibration testing machine / high temperature oven / vacuum oven / precision drying oven / incubator / Drying oven / large salt spray test chamber /